ZC-9800 is a dual-component plus forming liquid silicon rubber designed for electronics and electrical components. Such as the irrigation and encapsulation of the motor slot, micro transformer, and high -power LED drive power supply, which plays high temperature, heat conduction, insulation, sealing, waterproof, resistance to environmental pollution, eliminating stress, and preventing shocks. The purpose of the device.
Technical Index:
| Serial number | Project | Unit | Technical indicator | Detection standard | ||
| Before solidization |
1 |
Exterior |
Group A | - | Gray-white fluid | Visual inspection |
| Group B | - | Colorless and transparent | ||||
| 2 |
Viscosity |
Group A | mPa.s | 500-1500 | GB/T10247-2008 | |
| Group B | mPa.s | 250 | ||||
| 3 |
Density |
Group A | g/cm3 | 1.5-1.65 | GB/T13354-1992 | |
| Group B | g/cm3 | 0.97 | ||||
| 4 | Hybrid ratio(weight ratio) | - | 10:1 | - | ||
| 5 | Operation time | 25ºC | min | 30-60 | - | |
| 6 | Early solid time | 25ºC | h | 4-8 | - | |
| 7 | Heating and solidification | 100ºC | min | ≤30 | - | |
| After solidization |
8 | Exterior | - | Gray elastic boby | Visual inspection | |
| 9 | Solid density | g/cm3 | 1.4-1.6 | GB/T 533-2008 | ||
| 10 | Show's Harddness | Shore A | 45-60 | GB/T 5311-2008 | ||
| 11 | Volume resistivity | Ω•cm | ≥1*1013 | GB/T 1692-2008 | ||
| 12 | Dielectric strength | KV/mm | ≥15 | GB/T 1695-2005 | ||
| 13 | Flame retardant | - | V-0 | UL 94 | ||
| 14 | Thermal Conductivity | W/m.K | 0.4-0.6 | ASTM D5470 | ||
(1) Before the product is solidified, the liquidity is good, the operation time is moderate, and the operation (the two groups are mixed at 10: 1 ratio) are convenient.
(2)It can be used for a long time at -40 ºC ~ 200 ºC, with a small and high-temperature resistance with a small contraction rate and excellent resistance.
(3)It fully meets the EU ROHS instructions and meets the requirements of green environmental protection.
(4)There are two solidification methods: permanent mild moderate temperature, and deep -seated vulcanization in the inside and outside.
(5)It can maintain the original physical and electrical properties in various working environments, can resist the degradation of ozone and ultraviolet rays, and has good chemical stability.
This product is packed in 5kg and 20kg plastic barrels. Special packaging can be determined according to customer needs.